Had this idea to encapsulate colorful broken glass in a silver frame for a steampunk look. The kiln cycle went fine, but during cooling, the different expansion rates caused a hairline crack in the bezel. Now I'm staring at this fragile hybrid thing, wondering if annealing would have helped. What's your experience mixing materials with such different thermal behaviors? I'm tempted to try again with a lower melting point glass.